1. Direct replacement: This method can completely solve the problem of corrosion and leakage, but has the disadvantages of high price and long cycle. Corrosion will inevitably occur when the new water tank is in use, so it is not recommended for all manufacturers to use it.
2. Repair welding: This method is greatly affected by the manufacturer's welding process and component materials. Manufacturers with superior components and technology can do a good job of repairing and restore the water tank to normal use. If you are not proficient, it is easy to degrade the performance of the welded part and reduce the corrosion resistance, which will cause corrosion again.
3. Brushing epoxy resin anticorrosive material: Compared with the first two methods, this method is more economical and feasible, and the damage caused by the weld is less. It is a common choice for some manufacturers. However, due to the effect of surface adhesion and expansion coefficient performance, the brushed anti-corrosion protective layer often exhibits large-area peeling and cracking, and the effect is not ideal.
4. Brushing polymer composite materials: The polymer 1321 composite material launched in recent years has strong chemical corrosion resistance, high cohesiveness and versatility, and can deal with various corrosion and leakage problems of the water tank in time, compared with the previous three The method is more superior and can extend the service life of the equipment.
Through the above explanation, I believe that everyone has a general understanding of the treatment methods for the corrosion and leakage of the water tank welds. In addition to paying more attention to the price of Yancheng stainless steel water tank, people should also care about the quality of the water tank. When there is a problem, it is necessary to choose a suitable method for maintenance to ensure its long-term use.